Computers OverClocked Forums Computers OverClocked
"Not just another computer help website."

FAQ Search Upgrade Register
Favorite Threads Private Messaging Login

Menu
Forums
RegisterRegister
Over Clocking Guide
Over Clocking Help
Computer Building Help
Virus/Security Alerts
Broadband Tweaks
Computing Guides
Featured Hot Deals
Reviews
Tools


Top 25 reasons to register!

Advertise your link here for $19.99/month!

 
 Computers OverClocked Welcomes You!
 Date/Time is Sun Jun 24, 2018 10:41 am
 Computer Photo Gallery
Computing News Headlines:
New HTC Android Phones Tweaked to Evade Apple Patents
Ivy Bridge Temperatures – It’s Gettin’ Hot in Here
Adobe CS6 on sale today, Creative Cloud coming May 11th

Magnetic elimination method for 304 stainless steel castings
Post new topic Reply to topic Computers OverClocked Forums - The General Store All times are GMT - 5 Hours - EDT
Author Message
yaangcom
Member



User is offline 
Send private message
Joined: Apr 26 2016
Posts: 386

PostPost subject: Magnetic elimination method for 304 stainless steel castings
Posted: Sun May 27, 2018 5:45 am
Reply with quote

In many cases, the casting products produced by the 304 stainless steel, which are not magnetic, will have weak magnetic properties. What is the reason for it?
There are two main reasons, the first is the chemical composition of equivalent products are not suitable for the control of the manufacturer, usually in order to reduce production costs will be lower in the control of nickel content as low as possible, which is in the range of 8.0-8.2%, and the ratio of chromium and nickel to reach the corresponding value, the microstructure of stainless steel products will be generated a certain amount of ferrite and ferrite is magnetic; then through 1050-1080 DEG C solid solution could be completely dissolved into ferrite austenite to remove magnetic.
The second reason is cold working hardening. Austenitic stainless steel will generate deformation martensite when cold working. Deformation martensitic experience increases the strength of stainless steel, but the deformed martensite is magnetic. Of course, solid solution treatment or annealing can be used to remove deformed martensite, but the strength of the stainless steel is also reduced.
If you want to ensure cold working strength, but also to maintain weak magnetic or even no magnetic, the following degaussing method can be used.
The first is to reduce the ratio of chromium to nickel according to the principle of phase diagram, especially to increase the content of Ni Mn and so on to the upper limit. Before cold processing, the upper limit of solid solution treatment is made. Under the premise of ensuring the surface, the grain degree is 4 grade, and the magnetic properties of cold processing can be reduced.
The second is that the usual 304 stainless steel has a certain weak magnetic properties after cold processing. By knocking or in other ways, the austenite structure in it can be transformed into martensitic tissue, and a certain degree of magnetism will be made. When heated to 1050 degrees C, then water quenched and cooled, it can remove magnetic properties.
What needs to be understood is that the ratio of chromium / nickel to the corresponding ratio refers to the ratio of the two equivalent. When the chromium equivalent / nickel equivalent is below 0.9 of the single austenite, the stainless steel is not magnetic. Therefore, it can be seen from this aspect that the addition of nickel, manganese, nitrogen, or chromium reduction and silicon can all achieve the purpose of degaussing.
Source: China Stainless Steel Pipe Fittings Manufacturer - Yaang Pipe Industry Co., Limited (www.yaang.com)
Back to top
 Rate Post
View previous topic :: View next topic  
Post new topic Reply to topic Computers OverClocked Forums - The General Store Page 1 of 1


Similar Topics
Topic Author Forum Replies Posted
No new posts Factors affecting the wall thickness ... yaangcom The General Store 0 Thu Jun 21, 2018 6:15 am View latest post
No new posts Connection methods of stainless steel... yaangcom The General Store 0 Wed Jun 20, 2018 8:37 am View latest post
No new posts adding titanium in austenitic stainle... yaangcom The General Store 0 Tue Jun 19, 2018 9:29 am View latest post
No new posts Market Trajectory Of Global Stainless... Sebahtstian Hardware/Software Help, Questions and Information 0 Tue Jun 19, 2018 3:20 am View latest post
No new posts solid solution processing for stainle... yaangcom The General Store 0 Mon Jun 18, 2018 10:23 am View latest post